电气/电子应用性能特点 | |
用途 | |
加工方法 | |
多点数据 | Specific Heat vs. Temperature (ISO 11403-2) |
比重 | 1.04 | g/cm³ | ASTM D792 |
熔流率(220°C/10.0 kg) | 23 | g/10 min | ASTM D1238 |
收缩率 - 流动(3.20 mm) | 0.40 到 0.70 | % | ASTM D955 |
Dimensional Stability | 0.0 | % | ASTM D1042 |
洛氏硬度(R 计秤) | 110 | | ASTM D785 |
拉伸模量3(3.20 mm) | 2220 | MPa | ASTM D638 |
抗张强度4(屈服, 3.20 mm) | 51.0 | MPa | ASTM D638 |
伸长率4(断裂, 3.20 mm) | 30 | % | ASTM D638 |
弯曲模量5(3.20 mm) | 2750 | MPa | ASTM D790 |
弯曲强度5(3.20 mm) | 78.5 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | | | ASTM D256 |
-30°C, 3.20 mm | 78 | J/m | |
-30°C, 6.40 mm | 78 | J/m | |
23°C, 3.20 mm | 230 | J/m | |
23°C, 6.40 mm | 200 | J/m | |
热变形温度 | | | ASTM D648 |
0.45 MPa, 未退火, 6.40 mm | 90.0 | °C | |
1.8 MPa, 未退火, 6.40 mm | 86.0 | °C | |
维卡软化温度 | 94.0 | °C | ASTM D1525 |
RTI Elec | | | UL 746 |
1.50 mm | 95.0 | °C | |
3.00 mm | 100 | °C | |
RTI Imp | | | UL 746 |
1.50 mm | 95.0 | °C | |
3.00 mm | 100 | °C | |
RTI Str | | | UL 746 |
1.50 mm | 95.0 | °C | |
3.00 mm | 100 | °C | |
体积电阻率 | 1.0E+15 | ohm·cm | ASTM D257 |
介电强度 | 27 | kV/mm | ASTM D149 |
耐电弧性 | PLC 6 | | ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 0 | | UL 746 |
高电弧燃烧指数(HAI) | | | UL 746 |
1.50 mm | PLC 0 | | |
3.00 mm | PLC 1 | | |
高电压电弧起痕速率 (HVTR) | PLC 2 | | UL 746 |
热丝引燃 (HWI) | | | UL 746 |
1.50 mm | PLC 3 | | |
3.00 mm | PLC 3 | | |
UL 阻燃等级 | | | UL 94 |
1.50 mm, ALL | HB | | |
3.00 mm, ALL | HB | | |
干燥温度 | 80.0 | °C | |
干燥时间 | 2.0 到 4.0 | hr | |
螺筒后部温度 | 180 到 200 | °C | |
螺筒中部温度 | 190 到 210 | °C | |
螺筒前部温度 | 200 到 220 | °C | |
射嘴温度 | 200 到 230 | °C | |
加工(熔体)温度 | 210 到 240 | °C | |
模具温度 | 40.0 到 70.0 | °C | |
背压 | 29.4 到 58.8 | MPa | |
螺杆转速 | 30 到 60 | rpm | |